Hot rolled C1018, plenty strong enough but ductile enough to yield a bit if you bash it.
You can also use cold rolled but depending on what machining is done on it a piece of cold rolled can distort as the rolling stresses are relieved.
If you want easy machining use C12L14 it has a yield strength a bit below 1018 but is much easier to machine and, particularly, tap.