Looking for low-shrink solid hardwood advice

Results 1 to 5 of 5

Thread: Looking for low-shrink solid hardwood advice

  1. #1
    Member JerryBurks's Avatar
    Join Date
    Aug 2011
    Location
    USA
    Posts
    998
    Downloads
    0
    Uploads
    0

    Default Looking for low-shrink solid hardwood advice

    I am planning to build a pretty intricate wooden mechanism, not a clock but a combination lock for a chest. Of course I could use good quality plywood to avoid the inevitable shrink and expansion problem with humidity but for aesthetic reasons I would prefer nice solid hardwood.

    Can somebody give my a recommendation for a wood species that has proven to be good for clocks that is low shrink, reasonably hard, not splintering, machinable and obtainable in a well sorted hardwood lumber store? The parts will be rather small so it is O.K. if not cheap. I guess Teak and Padauk might qualify but I am not sure what else may be better. FWIW the parts will not be glued so no problem if oily.

    Thanks,

    JB

    Similar Threads:
    Puzzle, Finger Joint, Maze and Guilloche freeware at https://fabrikisto.com/tailmaker-software/


  2. #2
    Member
    Join Date
    Jun 2012
    Location
    usa
    Posts
    182
    Downloads
    0
    Uploads
    0

    Default

    Pressure casting with clear polyurethane would allow you to use any wood and not worry about shrinkage.

    Somewhere on this site should be the info you need for any wood species: Forest Products Laboratory - USDA Forest Service



  3. #3
    Registered
    Join Date
    Jul 2013
    Posts
    15
    Downloads
    0
    Uploads
    0

    Default

    Buy hard maple, and a pressure kit from www.packardwoodworks.com. Do it yourself, super easy


    Sent from my iPad using Tapatalk HD



  4. #4
    Member JerryBurks's Avatar
    Join Date
    Aug 2011
    Location
    USA
    Posts
    998
    Downloads
    0
    Uploads
    0

    Default

    Thanks guys, that sounds like it should work. I even have a good vacuum pump but did not think of vacuum impregnating the wood.

    The link examples were mostly for pen blanks but I guess I could do some 3/4" thick plates as well.

    I am wondering if I might have a chance stabilizing with thin epoxy resin, maybe when heated and really low viscosity? I still have a jug left over from another project.

    Puzzle, Finger Joint, Maze and Guilloche freeware at https://fabrikisto.com/tailmaker-software/


  5. #5
    Member ger21's Avatar
    Join Date
    Mar 2003
    Location
    Shelby Township
    Posts
    35538
    Downloads
    1
    Uploads
    0

    Default

    The problem with heating epoxy is that it will cure faster, especially if it's in a cup, or pot. As the curing reaction takes place, some epoxies can get hot enough to start a fire. You need to make sure you have a very slow setting epoxy.
    Depending on the wood species, most of the liquid will be drawn in through the end grain, and on larger sized pieces, you may not get enough penetration.

    The most stable wood will be wood that is quartersawn. Depending on the size of the parts, though, it may not make too much difference. Wood movement is measured as a percentage of growth or shrinkage, and for kiln dried hardwoods, it's typically going to be from 1%-5%. That's a very small amount for a small part. And if you live where's there's not a lot humidity most of the year, you might not see much movement at all.

    You might be better off choosing wood for it's strength, rather than stability. Depending on the application.

    Gerry

    UCCNC 2017 Screenset
    [URL]http://www.thecncwoodworker.com/2017.html[/URL]

    Mach3 2010 Screenset
    [URL]http://www.thecncwoodworker.com/2010.html[/URL]

    JointCAM - CNC Dovetails & Box Joints
    [URL]http://www.g-forcecnc.com/jointcam.html[/URL]

    (Note: The opinions expressed in this post are my own and are not necessarily those of CNCzone and its management)


Tags for this Thread

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
  •  


About CNCzone.com

    We are the largest and most active discussion forum for manufacturing industry. The site is 100% free to join and use, so join today!

Follow us on


Our Brands

Looking for low-shrink solid hardwood advice

Looking for low-shrink solid hardwood advice