Leeway,
I don't mind the cost of the media if it would do the job. How coarse do you think is "too" coarse for these bowls?
Originally Posted by Geof  Do you not like my technical terms? 
|
I am familiar with the technical terminology. However, I wasn't sure if you were using metric or English units of "horrible".
Would I mulitply or divide by 25.4?
Here's what I'm making. There is one more operation to do yet. The part will be attached using bolts through the slots. If the part is powdercoated, the paint will chip off when the bolts are snugged down. Thus the anodizing.
When it comes off the mill, there are no sharp corners as all deburring happens on the machine but I was hoping to get rid of most of the machining marks prior to anodizing.
Should I just blast these instead?